Mechanical Properties | Chemical Composition Max | Remarks | ||||||||
| Grade
|
Yield Point (YS) | Tensille Point (TS) | Elongation | Bend | Inside | C | Mn | P | S | C
Eq. |
|
|
|
MPa |
|
Angle | Radius | % | % | % | % | % | ||
|
|
|
|
min. % |
|
Of Bending |
|
|
|
|
|
|
| BJTP 280 | Min. 280 | Min 350 | 11 (d<=10mm) | 180
180 |
3,5d (d <= 16mm)
5d (d>=19mm) |
- | - | 0,05 | 0,05 | - | Hot Rolled Round Bars |
| Max. 405 | 12 (d>=12mm) | ||||||||||
| BJTS 280 | Min. 280 | Min 350 | 11 (d<=10mm) | 180
180 |
3,5d (d <= 16mm)
5d (d>=19mm) |
- | - | 0,05 | 0,05 | - | |
| Max. 405 | 12 (d>=13mm) | ||||||||||
| BJTS 420A | Min. 420 | Min. 525 | 9 (d<=19mm) | 180
180 180 |
3,5d (d <= 16mm)
|
0,32 | 1,65 | 0,05 | 0,05 | 0,60 | Hot Rolled Deformed Bars |
| Max. 545 | 8 (22<=d<25) | 5d (19 <= d <= 25) | |||||||||
| 7(d>=29mm) | 7d(29 <= d <= 36)
9d(d > 36mm) |
||||||||||
| BJTS 420B | Min. 420 | Min. 525 | 14(d<=19mm) | 180
180 180 |
3,5d(d<=19mm)
5d (19 <= d <= 25) 7d(29 <= d <= 36) 9d(d > 36mm) |
0,32 | 1,65
|
0,05 | 0,05 | 0,60 | |
| Max. 545 | 12(22<=d<25) | ||||||||||
| 10(d>36mm) | |||||||||||
| BJTS 520 | Min. 520 | Min. 650 | 7(d<=25mm) | 180
90 |
5d(d<=25mm)
7d(29<=d<=36) 9d(d>36mm) |
0,35 | 1,65 | 0,05 | 0,05 | 0,62 | |
| Max. 645 | 6(d>=29mm) | ||||||||||
| BJTS 550 | Min. 550 | Min. 688 | 7(d<=25mm) | 180
90 |
5d(d<=25mm)
7d(29<=d<=36) 9d(d>36mm) |
0,35 | 1,65 | 0,05 | 0,05 | 0,62 | |
| Max. 675 | 6(d>=29mm) | ||||||||||